Inconel 617

Inconel 617

Model No.:

UNS N06617; Alloy 617

Introduction:

Stock Forms: Round Bar, Rod

Product Detail

Product Tags

Inconel 617 is a solid-solution, nickel-chromium-cobalt-molydenum alloy with an exceptional combination of high-temperature strength and oxidation resistance. The alloy also has excellent resistance to a wide range of corrosive environment, and it is readily formed and welded by conventional techniques.

The high nickel and chromium contents make the alloy resistant to a variety of both reducing and oxidizing media. The aluminum, in conjunction with the chromium, provides oxidation resistance at high temperatures. Solid-solution strengthening is imparted by the cobalt and molydenum.

Inconel 617 Trade Name: Alloy 617; UNS NO6617;W.Nr.2.4663a;NiCr0Fer 617

Inconel 617 Chemaical composition:

Alloy

%

Ni

Cr

Fe

C

Mn

Si

Cu

Co

Ti

Al

P

S

617

Min.

44.5

20.0


0.05




10.0


0.80



Max.


24.0

3.0

0.15

1.0

1.0

0.5

15.0

0.60

1.50

0.015

0.015

Inconel 617 Physical properties

Density8.36g/cm³
Melting Point1332-1380

Inconel 617 Alloy minimum mechanical properties in the room temperature

Alloy state

Tensile strength
Rm N/mm²

Yield strength

R P0. 2N/mm²

Elongation

A 5 %

Brinell hardness

HB

Annealing treatment

780

300

45

-

Solution treatment

800

320

45

≤220

Inconel 617 Specifications:

Bar

Forging

Sheet

Strip

Pipe

Wire

ASTM B 166/ASME SB 166, SAE AMS 5887/DIN 17752

ASTM B564/ASME SB564 SAE AMS5887/DIN17754

ASTM B168/ASME SB 168/SAE AMS 5888 /SAE AMS 5889/ISO 6208/DIN 17750/AdTUV 485

ASTM B168/ASME SB 168/SAE AMS 5888 /SAE AMS 5889/ISO 6208/DIN 17750/AdTUV 485

ISO 6207 / ASTM B 546/ASME SB 546

/DIN 17751/AdTUV 485

ASTM B166/ASME SB166,DIN 17752

AWSA5.14/ERNiCrCoMo-1/AWS A5.11/ ENiCrCoMo-/ISO 9724

Inconel 617 Application field:

1.The combination of high strength and oxidation resistance at temperatures over 1800°F makes alloy 617 an attractive material for such components as ducting, combustion cans, and transition liner in both aircraft, and land based gas turbines.

2.Because of its resistance to high-temperature corrosion, the alloy is used for catalyst-grid supports in the production of nitric acid, for heat-treating baskets, and for reduction boats in the refining of molybdenum.

3.Alloy 617 also offers attractive properties for components of power-generating plants, both fossil-fueled and nuclear.